Product Feature
1. Physical peeling process, high purity graphene.
2. A physical insulated cladding layer can be formed on the surface of base material. Hence it can greatly improve paintings’ abrasive resistance and lifetime.
3. Thinner coating thickness and low cost.
4. Big diameter/thickness ratio and longer migration path for corrosive media to access base material.Hence the anti-corrosion performance is notably improved.
5. High carrier rate, excellent conductivity.
![SC Pas 2001c]( "SC Pas 2001c")
SEM _ Pas2002 paste dry film | ![SC Pas 2001c]( "SC Pas 2001c")
Pas2002 paste |
Application Case
Client request:
For conductive fabric coating, conductivity is desired to be improved by dosing certain amount graphene in the paste.
Test Plan & Result:
Specific resistance is notably reduced even minute quantity of FLG was added to paste.
![SC Pas 2001c]( "SC Pas 2001c")
Resistivity is reduced by adding FLG
Technical Parameters
Appearance | Graphene% | Solid% | Solvent | PH |
Ash Black sticky paste | 2.5±0.2% | 3.5±0.2% | De-ion water | Adjustable |
Recommendation
Application | Recommendation |
Water based paintings, water based conductive | Compared with carbon black and CNT, Graphene based conductive painting has lower surface resistance. Surface resistance of coating: 10e(+10) Ω/sq ( 0.5% graphene) and 10e(+4) Ω/sq (1.0% graphene) . |
Aqueous binder | Add 0.5% - 2% graphene, water/air penetration can be notably reduced while strength is enhanced. |
Water-based acrylic electromagnetic shielding additive | Add 2% graphene, coating surface resistance is as low as 10 Ω/sq, electromagnetic shielding is obviously promoted, and it keep good performance under high frequency situation. |
Package
Normally 20 kg packaged, or customized.